阐述了1Cr12Ni_3Mo_2VA马氏体不锈钢经不同温度回火的组织、碳化物的析出及位错结构。研究表明,采用1050℃保温60min空冷+650℃保温2h空冷能获得优良的综合性能。
tructurtes,precipitaion of carbides and dislocation structures in 1Cr1 2Ni3Mo2VA martensitic stainlesssteel at different tempering tempratures are explained. The study shows that adavantageous comblnationproporties are obtained after heat treating of austenization at 1050℃ for 1 hour and air queching to roomtemporature and aging at 650℃ for 2 hours air ccoling.