用阴极电沉积法在铝上获得了金黄色的钼酸盐转化膜,该膜具有良好的热稳定性。XPS和AES分析表明,膜厚约为1600A,膜表面的钼以Mo(Ⅳ)存在,而膜内则以Mo(Ⅳ)与Mo(Ⅳ)共存。从AES深度剥蚀曲线的组成恒定区求得膜的组成为:O55.7%,Mo27.6%,P11.2%,Al5.5%。
Golden molydate conversion film with high thermostability is obtained on aluminium by cathodic electrodeposition.XPS and AES analyses show that film thickness is about 1600A,and that Mo is existed as Mo(Ⅳ)in the film surface but as Mo(Ⅳ) and Mo(Ⅳ)in the internal layer of the film.The relative atomic percent content(A.C.%) of the film from the elemental composition constant region of the depth profile curves by AES is O 55.7% Mo 27.6%,Ph.2%,Al5.5% respectively.
出处
《电镀与涂饰》
CAS
CSCD
1994年第4期12-14,共3页
Electroplating & Finishing