在700℃与850℃的高温下,Fe_3Al金属间化合物表面形成了Al_2O_3保护膜,使其抗氧化性能远优于不妨钢,2%Cr(原子百分比)加入Fe_3Al会导致氧化过程初期氧化速率的增高,在熔融的硫酸盐和高压锅炉的烟气中,Fe_3Al的耐热腐蚀性能优于高温合金GH132.
At high temporature between 700℃ to 850℃,a protective film of Al2O3 forms at the sur-face of Fe3Al intermetallics, so that Fe3Al is more oxidation resistance than stainless steels,Additionof 2%Cr to Fe3Al results in the increase of oxidation rate at the initial stage of oxidation,In melted sulphates or smoke of high pressure boileres,Fe3Al has higher corrosion resistance than the superalloyGH132.