本文采用有机硅先驱体聚碳硅烷转化成碳化硅制备连续碳纤维增强的碳化硅基复合材料。对其制备工艺,如碳纤维体积分数的控制、液相浸渍聚碳硅烷热解转化成碳化硅基体的致密化等进行了研究。结果表明,该工艺对制备连续纤维增强的陶瓷基复合材料是一种有效的方法,易于实现纤维和基体的成型、复合。致密化过程不损伤纤维。对其C/SiC复合材料的性能进行了表征,C纤维具有明显增韧碳化硅的效果,其断裂机制表现为韧性特征。
SiC matrix composite was fabricated by using polycarbosilane as precursor andcontinous carbon fibers as reinforcer,The process of the fabrication such as polycarbosilanemolecular weight,control of fiber volume fraction,liquid impregnation and pyrolysis ofpolycarbosilane was investigated.The results show that the process is suitable to fabricationceramic matrix composite reinfoced with continuous fibers. Properties of the C/SiC composites were studied and the mechanism of fracture is toughfracture.
出处
《复合材料学报》
EI
CAS
CSCD
北大核心
1994年第3期26-32,共7页
Acta Materiae Compositae Sinica
关键词
碳化硅
碳纤维
复合材料
断裂韧性
polycarbosilane,silicon carbrid,carbon fiber,SiC matrix composite,fracture toughness