利用RFL热腐蚀试验装置,在温度为900℃,盐浓度20~100ppm,试验时间200小时的条件下,研究了三种具有不同硅分布形式的Al-Si涂层的抗热腐蚀性能。试验结果表明:涂层的抗热腐蚀性能与涂层中硅的分布形式密切相关。在涂层硅含量相当的情况下,硅呈内高外低的形式分布,可使涂层获得更佳的抗热腐蚀性能。
Hot corrosion behavior of three Al-Si coatings with different forms of silicon distribution was studied by RFL test apparatus at 900℃ in an atmosphere containing 20~100ppm salt.Total time of test was 200 hours.Experimental results showed that the corrosion resistance of these coatings was closely related to the silicon distribution in coatings. When coatings are well-matched in the silicon content,silicon distribu-tion is lower in the external zone and higher in the internal zone,it has the better hot corrosion behavior.