摘要
简要讨论了裂纹扩展率ｄａ／ｄＮ的实验数据分散的主要来源。提出了一种ｄａ／ｄＮ数据随机过程的区间分析方法，并用此方法分析了三组铝合金ＬＹ１２－ＣＺ＋ＣＳ的ｄａ／ｄＮ实验数据。分析结果表明，本文的处理方法是可行的；铝合金ＬＹ１２－ＣＺ＋ＣＳ在任意时刻的ｄａ／ｄＮ数据较好地服从Ｗｅｉｂｕｌｌ分布。
In this paper,the main sources of scatter of fatigue crack propagation rate da/dN are briefly dis-cussed.A new stochastic analysis method,interval analysis method,for describi ng da/dN was presented.andthen three groups of da/dN experimental data of LY12-CZ+CS Aluminium alloy are analysed using this method.The analytical results have shown that this new method is satisfactory and the da/dN of LY12-CZ+CS Alumini-um alloy obeys Weibull distribution.
出处
《机械强度》
CAS
CSCD
北大核心
1994年第1期43-45,共3页
Journal of Mechanical Strength
基金
航空科学基金
关键词
疲劳裂纹扩展
随机过程
铝合金
fatigue crack propagation , stochastic process,Aluminium alloy,probability,fracture mechanics,statistical analysis