摘要
从理论上分析了提高熔融石英水口质量的途径。试验结果表明:以优选的颗粒级配和NPS复合助剂,采用国内现有工艺,可生产出体积密度1.93—1.97g/cm3、耐压强度50—80MPa的高密度熔融石英水口。
Fused silica is used as main starting material with NPS compeite aid agent to prepare a fused silica nozzle by process ofslip coting and sintering. The nozzle has bulk density of 1. 93-- 1. 97g/cm3, CCS of 50--80MPa. The effect of grading andslurry properties on the finished product has also ben discussed.
出处
《耐火材料》
CAS
北大核心
1994年第3期162-164,共3页
Refractories
关键词
石英
水口
密度
耐火材料
Fused silica Nozzle Slip casting