摘要
Organo-soluble fluorinated polyimides were synthesized by the polycondensation of a new aromatic diamine α,α-bis(4-amino-3,5-dimethylphenyl)-4'-fluorophenyl methane with several aromatic dianhydrides.The one-step polymerizationprocedure was conducted at 180℃ in m-cresol,producing the polyimides with inherent viscosities of 0.68-0.76 dL.g^(-1).Thepolyimides could be soluble not only in polar aprotic solvents,such as N-methyl-2-pyrrolidinone,and N,N-dimethylacetamide,but also in common organic solvents,such as chloroform,cyclopentanone,m-cresol and so on.Thepolyimide films show excellent transparency with the UV-Vis cut-off lengths of 310-360 nm and light transmittances ofhigher than 80% in the visible region.In addition,the polyimides exhibit good thermal stability with an initial decompositiontemperature(T_d)higher than 530℃ and have more than 60% of residual weight retentions at 700℃.
Organo-soluble fluorinated polyimides were synthesized by the polycondensation of a new aromatic diamine α,α-bis(4-amino-3,5-dimethylphenyl)-4'-fluorophenyl methane with several aromatic dianhydrides.The one-step polymerizationprocedure was conducted at 180℃ in m-cresol,producing the polyimides with inherent viscosities of 0.68-0.76 dL.g^(-1).Thepolyimides could be soluble not only in polar aprotic solvents,such as N-methyl-2-pyrrolidinone,and N,N-dimethylacetamide,but also in common organic solvents,such as chloroform,cyclopentanone,m-cresol and so on.Thepolyimide films show excellent transparency with the UV-Vis cut-off lengths of 310-360 nm and light transmittances ofhigher than 80% in the visible region.In addition,the polyimides exhibit good thermal stability with an initial decompositiontemperature(T_d)higher than 530℃ and have more than 60% of residual weight retentions at 700℃.
基金
This work was supported by the National Natural Science Foundation of China(NSFC)for distinguished Young Scholars(No.59925310).