摘要
A novel soluble π-conjugated polymer, poly[(3-octanoylpyrrole-2,5-diyl)-p-(N,N-dimethylamino)benzylidene](POPDMABE), was synthesized firstly by the condensation of 3-octanoylpyrrole with para-dimethylaminobenzaldehyde. The chemical structure of the polymer was characterized by FTIR and 1H NMR spectrometries. The polymer is a potential nonlinear optical(NLO) material. According to the function of optical forbidden band gap(E_g) and photon energy(hν), the optical forbidden band gaps of the polymer before and after ion implantation were calculated. The resonant third-order nonlinear optical properties of POPDMABE before and after ion implantation were also studied by using the degenerate four-wave mixing(DFWM) technique at 532 nm. When the energy is 25 keV and the dose is 2.2×10 17 ions/cm 2, the {polymer′s} optical forbidden band gap is about 1.63 eV which is smaller than that of the non-implanted sample(1.98 eV) and the resonant third-order NLO susceptibility of POPDMABE is about 4.3×10 -7 esu, 1 order of magnitude higher than that of the non-implanted sample(4.1×10 -8 esu). The results show that nitrogen ion implantation is an effective method to improve the resonant third-order NLO property of the polymer.
A novel soluble π-conjugated polymer, poly[(3-octanoylpyrrole-2,5-diyl)-p-(N,N-dimethylamino)benzylidene](POPDMABE), was synthesized firstly by the condensation of 3-octanoylpyrrole with para-dimethylaminobenzaldehyde. The chemical structure of the polymer was characterized by FTIR and 1H NMR spectrometries. The polymer is a potential nonlinear optical(NLO) material. According to the function of optical forbidden band gap(E_g) and photon energy(hν), the optical forbidden band gaps of the polymer before and after ion implantation were calculated. The resonant third-order nonlinear optical properties of POPDMABE before and after ion implantation were also studied by using the degenerate four-wave mixing(DFWM) technique at 532 nm. When the energy is 25 keV and the dose is 2.2×10 17 ions/cm 2, the {polymer′s} optical forbidden band gap is about 1.63 eV which is smaller than that of the non-implanted sample(1.98 eV) and the resonant third-order NLO susceptibility of POPDMABE is about 4.3×10 -7 esu, 1 order of magnitude higher than that of the non-implanted sample(4.1×10 -8 esu). The results show that nitrogen ion implantation is an effective method to improve the resonant third-order NLO property of the polymer.
基金
theNationalNaturalScienceFoundationofChina(No.60277002).