A novel soluble π-conjugated polymer, poly[(3-octanoylpyrrole-2,5-diyl)-p-nitrobenzylidene] (POPNBE), was synthesized by a five-step reaction. As a result of introducing a long acyl to pyrrole at 3-position, the polymer can be easily solved in polar solvents and be processed into films. The chemical structures of the intermediates and POPNBE were characterized by FTIR, 1H NMR, and UV-Vis-NIR spectrometries. The absorption band in the range of 400-600 nm in the UV-Vis-NIR spectrum is due to the π-π * band gap transition. The optical band gap of POPNBE obtained from the optical absorption is about 1.72 eV. The resonant third-order nonlinear optical property of POPNBE at 532 nm was studied by using the degenerate four-wave mixing(DFWM) technique. The resonant third-order nonlinear optical susceptibility of POPNBE is about 3.42×10 -8 esu.
A novel soluble π-conjugated polymer, poly[(3-octanoylpyrrole-2,5-diyl)-p-nitrobenzylidene] (POPNBE), was synthesized by a five-step reaction. As a result of introducing a long acyl to pyrrole at 3-position, the polymer can be easily solved in polar solvents and be processed into films. The chemical structures of the intermediates and POPNBE were characterized by FTIR, 1H NMR, and UV-Vis-NIR spectrometries. The absorption band in the range of 400-600 nm in the UV-Vis-NIR spectrum is due to the π-π * band gap transition. The optical band gap of POPNBE obtained from the optical absorption is about 1.72 eV. The resonant third-order nonlinear optical property of POPNBE at 532 nm was studied by using the degenerate four-wave mixing(DFWM) technique. The resonant third-order nonlinear optical susceptibility of POPNBE is about 3.42×10 -8 esu.
基金
theNationalNaturalScienceFoundationofChina(No.60277002).