V_2O_5/TiO_2催化剂表面结构FT-IR发射光谱研究(Ⅱ) 被引量:6

FT-IR Emission Spectroscopic Studies of Surface Structure of V_2O_5/TiO_2 Catalyst
下载PDF
导出
摘要 用傅里哀变换红外发射光谱原位考察了V_2O_5/TiO_2催化剂在制备焙烧过程中担载偏钒酸铵的热分解步骤及其形成的表面活性相结构。偏钒酸铵在200℃左右分解,在300℃之前完全转化为晶相V_2O_5。担载于TiO_2上的偏钒酸铵在100℃左右与TiO_2已产生强的化学作用,在200℃之前已完全分解。对于10%(质量分数)V_2O_5/TiO_2催化剂其担载偏钒酸分解后在1020cm^(-1)附近出现晶相V_2O_5的特征峰。但在500℃进一步焙烧后晶相V_5O_5的峰减弱并在1025—900cm^(-1)区出现宽峰,表明部分晶相V_2O_5可能转化为二维高分散的VO_x物种。2%(质量分数)V_2O_5/TiO_2催化剂在焙烧过程中也显示晶相V_2O_5的弱峰,但同时也观察到属于VO_x物种的宽峰。进一步降低钒担载量,V_2O_5晶相特征峰逐渐消失,而在1025—900cm^(-1)区出现二维VO_x物种的宽峰。结果还表明傅里衰变换红外发射光谱是表征氧化物催化剂表面相结构的一种有力的方法。 FT-IR emission spectroscopy has been used to study the surface structure of V_2O_5/TiO_2 catalyst with V_2O_5 loadings of 0.4%, 2% and 10% wt. prepared by impregnation of TiO_2 in NH_4VO_3 solution. The IR emission spectra were recorded insitu durinbg the course of a calcination of the impregnated catalyst from 100℃ to 500℃. The ammonium vanadate supported on TiO_2 was found to be decomposition more easily than pure NH_4VO_3 most possibly owing to the chemical interaction between vanadate and TiO_2. For 10% wt. V_2O_5/TiO_2 catalyst the IR peaks due to V_2O_5 phase appeared as the catalyst was calcined at 200-400℃. when the catalyst was calcined at 500℃ the peaks of V_2O_5 phase were evidently reduced indicating that the part of V_2O_5 phase probably spreaded into highly dispersed vanadium oxide on TiO_2. For the catalysts with lower loading of vanadium, the IR peaks due to V_2O_5 phase decreased and a broad peak ranging from 1050cm^(-1) to 900cm^(-1) became prominent especially after a calcination at 500℃. The broad peak was tentatively assigned to the highly dispersed VO_x species which might be the two-dimensional vanadium oxide. This study also demonstrated that FT-IR emission spectroscopy is a very sensitive technique for investigating the surface structure of metal oxide catalyst.
出处 《物理化学学报》 SCIE CAS CSCD 北大核心 1994年第1期33-37,共5页 Acta Physico-Chimica Sinica
基金 国家自然科学基金
关键词 红外发射光谱 氧化物催化剂 FT-IR emission spectroscopy, Catalyst characterization, V_2O_5/TiO_2, Surface structure.
  • 相关文献

参考文献6

  • 1李灿,Appl Spectrosc,1993年,47卷,56页
  • 2李灿,1992年
  • 3李灿,物理化学学报,1992年,8卷,64页
  • 4李灿,Appl Spectrosc,1991年,45卷,874页
  • 5李灿,石油化工,1991年,20卷,801页
  • 6Chan S S,J Phys Chem,1984年,88卷,5831页

同被引文献261

引证文献6

二级引证文献29

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部