This note mainly reports a successful preparation of a alumina-pillared layered titanate with a high interlayer spacing through a step-wise exchange process. X-ray diffeaction patterns indicate that the resultant alumina-pillared layered titanate has an interlayer spacing of 1.70 nm, which is 0.17 nm higher than that of previously reported,and has a thermal stability over 500℃. The surface area (N2,BET method) of the product is determined to be 72.4 m2.g-1. The N2 adsorption and desorption isotherm of the product demonstrates that the resultant alumina-pillared layered titanate is porous, with both thecropores and mesopores.
This note mainly reports a successful preparation of a alumina-pillared layered titanate with a high interlayer spacing through a step-wise exchange process. X-ray diffeaction patterns indicate that the resultant alumina-pillared layered titanate has an interlayer spacing of 1.70 nm, which is 0.17 nm higher than that of previously reported,and has a thermal stability over 500℃. The surface area (N2,BET method) of the product is determined to be 72.4 m2.g-1. The N2 adsorption and desorption isotherm of the product demonstrates that the resultant alumina-pillared layered titanate is porous, with both thecropores and mesopores.
出处
《物理化学学报》
SCIE
CAS
CSCD
北大核心
1994年第2期100-102,共3页
Acta Physico-Chimica Sinica
关键词
高层间距
氧化铝
柱层状
钛酸盐
High interlayer spacing, Alumina-pillared layered titanate, Preparation and characterization