摘要
介绍了轧辊存在剥落、断裂、裂纹等几种失效方式,并重点分析了轧辊剥落和断裂产生的机理,为分析生产实践中轧辊失效原因和采取相应改进措施以提高轧辊使用寿命提供了依据。
The failure types of roll such as flaking, fracture, crack etc are described. The mechanism of flaking and fracture of roll is analyzed. The preventive measures for roll failure and failure causes are found in practice, and prolonging service life of roll.
出处
《山东冶金》
CAS
2005年第1期31-33,共3页
Shandong Metallurgy
关键词
轧辊
失效原因
剥落
断裂
裂纹
roll
failure cause
flaking
fracture
crack