CaO-Al_2O_3-SiO_2 系统微晶玻璃作为微晶玻璃中的一个新品种,具有非常鲜明的特点。本文讨论了在CaO-Al_2O_3-SiO_2 系统微晶玻璃中加入ZrO_2,研究了ZrO_2 对CaO-Al_2O_3-SiO_2系统微晶玻璃烧结的影响。随着ZrO2 加入量的增加,玻璃颗粒的烧结收缩率下降,说明ZrO_2 的加入对玻璃颗粒的烧结收缩有一定的阻碍作用。ZrO_2的加入对CaO-Al_2O_3-SiO_2 系统微晶玻璃中的主晶相(β-硅灰石晶体)的析出没有大的影响。
Being a new variety, CaO-Al_2O_3-SiO_2 glass-ceramic is outstandingly characterized and widely used. This paper discusses the addition of ZrO_2 into CaO-Al_2O_3-SiO_2 glass-ceramic and the influence of ZrO_2 on sintering process of CaO-Al_2O_3-SiO_2 glass ceramics. As the ZrO_2 increases, the shrinkage ratio of glass particle will decrease. Such phenomenon indicates that ZrO_2 has a baffling effect on sintering shrinkage ratio of glass particle. Increase of sintering temperature significantly conduces to descending the liquid phase viscosity of glass particles, which consequently is available for sintering. The addition of ZrO_2 has little effect on crystallization of main crystalline phase (β- wollastonite).
出处
《玻璃与搪瓷》
CAS
2005年第2期14-17,共4页
Glass & Enamel
基金
国家自然科学基金资助项目(50272043)
湖北省自然科学基金资助项目(2002AB077)
武汉理工大学硅酸盐材料教育部重点实验室基金资助项目(SYSJJ2002-08)
武汉理工大学校基金资助项目(2003XJJ013)。