摘要
The properties of anti-seismic HRB400 steel bars with 25 mm diameter were systematically investigated. The results showed that the properties of the HRB400 reinforced steel bars had been greatly enhanced comparing with HRB335 steel bars, i.e. coordination of strength and ductility, strain-aging sensibility, low temperature impact toughness, weld ability and high strain low cycle fatigue. The ductile-brittle transit temperatures of hot-rolled and strain-aged steel bars were evaluated as –17 °C and ?8 °C respectively, and the low temperature impact toughness of HRB400 steel bars remains to be improved. Transmission electron microscopy (TEM) and electron diffraction showed little vanadium existed in ferrite as VN, most of which existed in pearlite as alloy cementite which resulted in the declination of impact toughness. Methods were suggested to improve the anti- seismic properties of steel bars.
The properties of anti-seismic HRB400 steel bars with 25 mm diameter were systematically investigated. The results showed that the properties of the HRB400 reinforced steel bars had been greatly enhanced comparing with HRB335 steel bars, i.e. coordination of strength and ductility, strain-aging sensibility, low temperature impact toughness, weld ability and high strain low cycle fatigue. The ductile-brittle transit temperatures of hot-rolled and strain-aged steel bars were evaluated as –17 °C and ?8 °C respectively, and the low temperature impact toughness of HRB400 steel bars remains to be improved. Transmission electron microscopy (TEM) and electron diffraction showed little vanadium existed in ferrite as VN, most of which existed in pearlite as alloy cementite which resulted in the declination of impact toughness. Methods were suggested to improve the anti- seismic properties of steel bars.