The effect of sintering dispersed and bulk,low molecular weight(M_n=50,000 Da),nano-emulsionpolytetrafluoroethylene(PTFE)particles near their melting point is described.With the nascent particles consisting of ca.75 nm diameter,hexagonal,single crystals,sintering at,e.g.,350℃,results,initially,in merger of neighboring particles,followed by individual molecular motion on the substrate and the formation of folded chain,lamellar single crystals andspherulites,and on-edge ribbons.It is suggested these structures develop,with time,in the mesomorphic“melt”.Sintering ofthe bulk resin yields extended chain,band structures,as well as folded chain lamellae;end-surface to end-surface merger,possibly by end-to-end polymerization,occurs with increasing time.
The effect of sintering dispersed and bulk,low molecular weight(M_n=50,000 Da),nano-emulsionpolytetrafluoroethylene(PTFE)particles near their melting point is described.With the nascent particles consisting of ca.75 nm diameter,hexagonal,single crystals,sintering at,e.g.,350℃,results,initially,in merger of neighboring particles,followed by individual molecular motion on the substrate and the formation of folded chain,lamellar single crystals andspherulites,and on-edge ribbons.It is suggested these structures develop,with time,in the mesomorphic“melt”.Sintering ofthe bulk resin yields extended chain,band structures,as well as folded chain lamellae;end-surface to end-surface merger,possibly by end-to-end polymerization,occurs with increasing time.