摘要
By adding small amount of TiO2, aluminum slag could be used to synthesize cor- dierite. α-Al2O3, TiO2 and dehydrated talc could generate solid solution to accelerate the solid-state reaction to form cordierite. The experimental results show that the content of cordierite increases with the increase of TiO2 added. 3.0% of TiO2 is determined to be the best amount, because all crystalline substances are converted into cordierite at this content. Philips X’pert plus software analysis shows that when the content of TiO2 is from 0 to 1.0%, cordierite has the same hexagonal structure as the single crystal and the lattice parameters change slightly; when the content of TiO2 is from 1.0 to 2.0%, the cordierite still keeps hexagonal structure but the lattice parameters change greatly; when the content of TiO2 is from 2.0 to 3.5%, the cordierite is converted from hexagonal into rhombic and the lattice parameters change accordingly.
By adding small amount of TiO2, aluminum slag could be used to synthesize cor- dierite. α-Al2O3, TiO2 and dehydrated talc could generate solid solution to accelerate the solid-state reaction to form cordierite. The experimental results show that the content of cordierite increases with the increase of TiO2 added. 3.0% of TiO2 is determined to be the best amount, because all crystalline substances are converted into cordierite at this content. Philips X’pert plus software analysis shows that when the content of TiO2 is from 0 to 1.0%, cordierite has the same hexagonal structure as the single crystal and the lattice parameters change slightly; when the content of TiO2 is from 1.0 to 2.0%, the cordierite still keeps hexagonal structure but the lattice parameters change greatly; when the content of TiO2 is from 2.0 to 3.5%, the cordierite is converted from hexagonal into rhombic and the lattice parameters change accordingly.
基金
This project was supported by the 863 Project (2003AA322020)