Grain refinement of superalloy K4169 was achieved by adding refiners into the alloy melt and their effects on the mechanical properties were investigated. The tensile properties at room temperature and 700 ℃ and low cycle fatigue properties at room temperature were compared for both conventional and fine grained test bars. The results indicate that the rupture strength, yield strength, elongation and reduction of area for refined grains are all much superior to those for coarse ones. Whereas the elongation and reduction of area of fine grained samples decrease at 700 ℃. Low cycle fatigue properties of samples with refined grains at room temperature are improved significantly. In addition, the degree of dispersion of low cycle fatigue data of samples with refined grains is diminished.
Grain refinement of superalloy K4169 was achieved by adding refiners into the alloy melt and their effects on the mechanical properties were investigated. The tensile properties at room temperature and 700 ℃ and low cycle fatigue properties at room temperature were compared for both conventional and fine grained test bars. The results indicate that the rupture strength, yield strength, elongation and reduction of area for refined grains are all much superior to those for coarse ones. Whereas the elongation and reduction of area of fine grained samples decrease at 700 ℃. Low cycle fatigue properties of samples with refined grains at room temperature are improved significantly. In addition, the degree of dispersion of low cycle fatigue data of samples with refined grains is diminished.
出处
《中国有色金属学会会刊：英文版》
CSCD
2005年第2期280-285,共6页
Transactions of Nonferrous Metals Society of China
基金
Project(G2000067202) supported by the National Basic Research Program of China