摘要
Field emission-scanning electron microscopy(FE-SEM) technique was employed to observe the shape, size and distribution of AlN+MnS inclusions in oriented electrical steels. Specimens used for FE-SEM observation were deeply electrolytic etched at room temperature in non-aqueous acetylacetone(AA) solution. The results indicate that the FE-SEM technique has obvious advantage in specimen preparation. Therefore, it can be easily used to identify the AlN+MnS inclusions and even copper nano-particles in oriented electrical steels with the same analysis accuracy as that by TEM. This technique is a good substitute for TEM and the associated specimen preparation in the observation of inclusions in electrical steels. It will be a powerful technique for routine analysis in the production of grain oriented electrical steels.
Field emission-scanning electron microscopy(FE-SEM) technique was employed to observe the shape, size and distribution of AlN+MnS inclusions in oriented electrical steels. Specimens used for FE-SEM observation were deeply electrolytic etched at room temperature in non-aqueous acetylacetone(AA) solution. The results indicate that the FE-SEM technique has obvious advantage in specimen preparation. Therefore, it can be easily used to identify the AlN+MnS inclusions and even copper nano-particles in oriented electrical steels with the same analysis accuracy as that by TEM. This technique is a good substitute for TEM and the associated specimen preparation in the observation of inclusions in electrical steels. It will be a powerful technique for routine analysis in the production of grain oriented electrical steels.
出处
《中国有色金属学会会刊：英文版》
EI
CSCD
2005年第2期460-463,共4页
Transactions of Nonferrous Metals Society of China
基金
Project(50471104) supported by the National Natural Science Foundation of China
关键词
定向铁心硅钢
场发射-扫描电子显微镜
杂质成分
相观测
oriented electrical steels
field emission-scanning electron microscopy(FE-SEM)
inclusions