摘要
采用高温固相法在弱还原气氛下制备了掺入Tb3+的SrAl2O4:Eu2+,Dy3+磷光体。研究了Tb3+对SrAl2O4:Eu2+,Dy3+磷光体的发光性能的影响。结果发现,引入Tb3+以后,对基质SrAl2O4 的晶体结构基本上没有影响,也未改变磷光体的发光光谱,却使磷光体的初始亮度显著提高,并使余辉时间延长。其余辉强度随时间的变化由最初的快衰减过程和随后的慢衰减过程组成,符合t-1. 1的双曲线规律。并初步探讨了Tb3+的作用机制。
Tb 3+ doped SrAl_2O_4:Eu 2+ ,Dy 3+ phosphor has been synthesized. Tb 3+ doped into the phosphor as an impurity, does not change the main crystalline structure and the emission spectrum, but improves the light intensity and the light-lasting time and makes the phosphor possess a longer persistent afterglow characteristic with hyperbola type decay (the radiant intensity t -1.1 ). The explanation of the luminescent mechanism of Tb 3+ doped SrAl_2O_4:Eu 2+ ,Dy 3+ was presented.