摘要
安庆分公司储运部501号、502号柴油罐顶局部减薄严重至穿孔。经分析这两台柴油罐无保温且储油温度较高,同时炼油装置加工的为高含硫原油。该文对腐蚀现象进行分析,认为是露点腐蚀造成的,并提出了防护措施。
The 501# ,502# ,diesel fuel tank roof thinned locally and even perforated at severe local. By means of analysis, two set diesel fuel talks were without thermal insulation, and the temperature of storage fuel was higher,the processing oil in the refining unit was high sulphureous crude oil. In this article,the corrosion phenomenon was analyzed, and recognized that it was caused by dew point corrosion. The protection was proposed.