The influence of permanent-magnet-driven stirring during solidification on the microstructure and corrosion property of AZ61 magnesium alloy was investigated. The corrosion behaviour of AZ61 was studied in 3.5mol/L NaCl by measuring electrochemical polarization. The results show that the permanent-magnet stirring refines the microstructure of AZ61 magnesium alloy, which improves the precipitation amount and distribution uniformity of β phase and decreases the content of hydrogen, but it has less influence on the distribution uniformity of Zn. The change of precipitation amount of β phase influences the corrosive nature of the matrix, and it has no direct proportion with the corrosion resistance of the matrix.
The influence of permanent-magnet-driven stirring during solidification on the microstructure and corrosion property of AZ61 magnesium alloy was investigated. The corrosion behaviour of AZ61 was studied in ~3.5 ~mol/L NaCl by measuring electrochemical polarization. The results show that the permanent-magnet stirring refines the microstructure of AZ61 magnesium alloy, which improves the precipitation amount and distribution uniformity of β phase and decreases the content of hydrogen, but it has less influence on the distribution uniformity of Zn. The change of precipitation amount of β phase influences the corrosive nature of the matrix, and it has no direct proportion with the corrosion resistance of the matrix.
出处
《中国有色金属学会会刊：英文版》
CSCD
2005年第3期536-541,共6页
Transactions of Nonferrous Metals Society of China
基金
Projects(50234020
50475157)supportedbytheNationalNaturalScienceFoundationofChina
Project(105052)supportedbytheMinistryofEducationofChina