0前言 滚动轴承套圈(滚珠滚动槽)由于与滚动体形成点或线接触，循环作用的接触应力可高达n GPa。近年来，由于轴承的使用环境多为高温、高表面压力、高速旋转、振动条件下等的恶劣环境。由于循环应力的作用引起材质疲劳而导致出现了各种组织的变化，诸如在滚道压痕部形成黑色组织(Dark Etching Constituent：DEC，Dark：EtchingArea：DEA，
同被引文献6
-
1Vegter R H, Slycke J T. The Role of Hydrogen on Roll- ing Contact Fatigue Response of Rolling Element Bear- ings [ J ]. Journal of ASTM International, 2010,7 ( 2 ) : 1 -10.
-
2阎承东.真空与可控气氛热处理[M].北京:化学工业出版社,2006.
-
3Kenji Tamada, Hiromasa Tanaka, Noriyuki Tsushima. A New Type of Flaking Failure in Bearing for Electrical Instruments of Automotive Engines [ J ]. Journal ofASTM International, 1998, STP1327 : 167 - 184.
-
4Murakami Yukitaka, Yokoyama Naoka N . Influence of Hydrogen Trapped by Inclusions on Fatigue Strength of Bearing Steel [ J]. Journal of ASTM International, 2002 ,STP1419 : 113 - 122.
-
5Takayuki kawamura, Hidenobu Mikami. Development of NA103A Long - Life Grease for Automotive Components [J]. NTN Technical Review,2007 (75) : 116 - 122.
-
6Hiroshi Hamada, Yukio Matsubara. The Influence of Hydrogen on Tension - Compression and Rolling Contact Fatigue Properties of Bearing Steel [ J ]. NTN Technical Review,2006 (74) : 54 - 60.
二级引证文献2
-
1刘日宣,李兴林,常振,季英昌,吴加锹.汽车交流发电机轴承早期失效原因分析[J].哈尔滨轴承,2019,40(3):33-37. 被引量：1
-
2吴志伟,杨卯生,赵昆渝.高合金表面硬化轴承钢的滚动接触疲劳行为研究[J].表面技术,2021,50(7):283-294. 被引量：2
-
1原田久,彭涛,江涛.滚动接触条件下轴承钢中白色组织的产生过程[J].国外轴承技术,2004(3):48-54.
-
2杨升富.A-dec牙科综合治疗椅故障分析与维修[J].医疗卫生装备,2012,33(3):145-146. 被引量：7
-
3张曜,谢廷林.100Cr6钢制轴承套圈表面屈氏体含量超标的原因分析[J].轴承,2009(12):35-36.
-
4王晓卨.套螺母镀锌缺陷的原因分析[J].理化检验（物理分册）,2001,37(8):357-359. 被引量：1
-
5木野伸郎,蒋修治(译),江涛(校).氢对滚动疲劳寿命的影响及其对策[J].国外轴承技术,2005(4):31-35.
-
6孔令辉.PLC在啤酒发酵控制中的应用[J].自动化仪表,2002,23(11):38-40. 被引量：4
-
7刘斌,牛玉周,郭长建.发电机轴承中白色组织剥落现象的探讨[J].轴承,2012(9):29-32. 被引量：2
-
8彭龑,何玉林.Euclid-Is二次开发实践[J].工程设计CAD及自动化,2000(6):56-57.
-
9林鸿海,黄金朋,林翔.有限元法分析空心后向反射器面形精度[J].光学技术,2000,26(2):169-171. 被引量：2
-
10刘玉琳.非对称应力循环作用下构件疲劳强度的计算[J].郑州轻工业学院学报,1994,9(1):35-38.