The effect of trace Ti and Y on Au-based alloys with 990 fineness has beeninvestigated systematically by means of tensile test, hardness test, scanning and transmissionelectron microscopic analyses. These experimental results show that trace Ti and Y can significantlyimprove the mechanical properties of Au-based alloys with 990 fineness because Ti and Y cansignificantly refine matrix grains, and solid solution strengthening, work strengthening andprecipitation strengthening occur during mechanical heat treatment.
The effect of trace Ti and Y on Au-based alloys with 990 fineness has beeninvestigated systematically by means of tensile test, hardness test, scanning and transmissionelectron microscopic analyses. These experimental results show that trace Ti and Y can significantlyimprove the mechanical properties of Au-based alloys with 990 fineness because Ti and Y cansignificantly refine matrix grains, and solid solution strengthening, work strengthening andprecipitation strengthening occur during mechanical heat treatment.
基金
This work is financially supported by the Key Scientific and Technological Project of Hubei Province (No. 971P0216).