摘要
通过对不锈钢管道的材质、介质、腐蚀产物、金相试验等分析,寻找产生裂纹的原因。材质不良、氯离子介质环境是造成不锈钢腐蚀失效的主要原因。
The material, dielectric environment, corrosion products, microscopic test of stainless steel pipe were analysised inthis article. The cause of cracking was found. The defective material, chlorideion environment were the prime reasons of stainlesscorrosion damage.
出处
《全面腐蚀控制》
2005年第3期30-32,共3页
Total Corrosion Control