摘要
A novel ordered reactive oligomeric ladderlike copolymethyl-aminopropylsilsesquioxane(Me-AP-T),was successfully synthesized by an efficient hydrosilylation graft reaction of 1,1,1-trimethyl-N-2-propenyl-silanamine with a reactive oligomeric ladderlike copolymethyl-hydrosilsesquioxane(Me-H-T),which was prepared by“supramolecular chemistry-dictated stepwise coupling polymerization”process.FT-IR,~1H-and ^(29)Si-NMR spectra show that hydrosilylation reaction proceeds completely.Moreover,~1H-NMR spectra also indicate that both the molar ratios of≡SiMe group to Si—H and≡SiMe group to≡SiPrNH_2 are approximately 1:1 respectively based on the ratio of integrated resonance areas of the different groups.XRD analysis and ^(29)Si-NMR spectra are used for investigating the ladderlike structure of the polymers.A high T_g(128.38℃)of Me-AP-T shown in DSC measurement implies that the ordered reactive Me-AP-T macromolecules have much stiff chains.
A novel ordered reactive oligomeric ladderlike copolymethyl-aminopropylsilsesquioxane(Me-AP-T),was successfully synthesized by an efficient hydrosilylation graft reaction of 1,1,1-trimethyl-N-2-propenyl-silanamine with a reactive oligomeric ladderlike copolymethyl-hydrosilsesquioxane(Me-H-T),which was prepared by“supramolecular chemistry-dictated stepwise coupling polymerization”process.FT-IR,~1H-and ^(29)Si-NMR spectra show that hydrosilylation reaction proceeds completely.Moreover,~1H-NMR spectra also indicate that both the molar ratios of≡SiMe group to Si—H and≡SiMe group to≡SiPrNH_2 are approximately 1:1 respectively based on the ratio of integrated resonance areas of the different groups.XRD analysis and ^(29)Si-NMR spectra are used for investigating the ladderlike structure of the polymers.A high T_g(128.38℃)of Me-AP-T shown in DSC measurement implies that the ordered reactive Me-AP-T macromolecules have much stiff chains.
基金
This work was supported by the National Natural Science Foundation of China(Nos.50273043,20204016,20174047)