Recent development in the modification of ceria-based catalysts for exhaust gas treatment was reviewed with the dependence of redox properties on structural characters of materials. The doping of ceria with different cations such as rare earth or transition metal oxides results in improvement of structural stability, catalytic function and resistance to sintering at high temperatures. Aging and reduction treatment at high temperatures promote ceria reduction and is beneficial for oxygen storage capacity of the three-way catalysts. Chemical filing technique is very effective in modifying the redox property in the low temperature regions.
Recent development in the modification of ceria-based catalysts for exhaust gas treatment was reviewed with the dependence of redox properties on structural characters of materials. The doping of ceria with different cations such as rare earth or transition metal oxides results in improvement of structural stability, catalytic function and resistance to sintering at high temperatures. Aging and reduction treatment at high temperatures promote ceria reduction and is beneficial for oxygen storage capacity of the three-way catalysts. Chemical filing technique is very effective in modifying the redox property in the low temperature regions.
基金
theNationalHighTechnologyResearchandDevelopmentProgramofChina (863Program )(2 0 0 2AA64 3 0 10 )