银钎剂水溶法改性制备工艺的优化 被引量:1

Optimization of water dissolution modification process using silver brazing fluxes
下载PDF
导出
摘要 针对银钎剂生产成本较高、性能不够稳定以至难以大批量生产的现状,通过在银钎剂的水溶法改性工艺的基础上,采用正交试验法对其工艺及配方进行了优化设计。正交试验表明,烘干时间对钎剂性能的影响最为显著,其次是成分配比,再次是烘干温度。水溶法改性最佳方案是,钎剂配比为42%KF+23%KBF4+35%B2O3,烘干时间为45 m in,烘干温度为350℃。实施了优选的工艺其操作方便、生产成本低、产品质量稳定。 The optimization of the water dissolution process using silver brazing fluxes was conducted by orthogonal test. The test result showed that effect of bake time on flux property is the best notable, next proportioning of compositions affected flux property, then bake temperature affected flux property. The optimum process parameters are component of 42%KF+23%KBF4+35%B2O3, bake time of 45 min and bake temperature of 350°C. By using the silver brazing fluxes, the best results of the jointing can be carried out.
出处 《焊接学报》 EI CAS CSCD 北大核心 2005年第7期75-76,80,共3页 Transactions of The China Welding Institution
关键词 银钎剂 正交试验 吸湿性 熔点 铺展性 Copper Dissolution Optimization Statistical methods Welds X ray diffraction analysis
  • 相关文献

参考文献3

  • 1Phil Roberts. A fresh look at low temperature silver brazing[J]. Welding & Metal Fabrication, 1997, 65(4): 26-29.
  • 2伍成根,张露菁.银钎剂的改性处理[J].焊接,2002(10):29-31. 被引量:4
  • 3天津化工研究院.无机盐工业手册[M].北京:化学工业出版社,1979.730-734,522-578.

二级参考文献3

  • 1天津化工研究院.无机盐工业手册[M].北京:化学工业出版社,1979.730-734,522-578.
  • 2张启运 庄鸿寿.钎焊手册[M].北京:机械工业出版社,1998..
  • 3张露菁,朱庆华,顾润南.银钎剂剖析与制备的研究[J].中国纺织大学学报,1999,25(1):98-99. 被引量:2

共引文献23

同被引文献1

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部