摘要
以填充聚硅氮烷的室温硫化型硅橡胶(RTV),在室温下硫化制得的硫化胶,与常规填充SiO2的RTV硫化胶进行了比较,试验结果表明,前者的物理机械性能优于后者;热老化性能(热空气250℃下,经48h),前者保持柔软,拉伸强度保持原来的70%以上,而后者则完全老化,丧失性能。
The mechanical properties and heat stability of room temperature vulcanized silicone rubber were improved by polysilazane. The results showed that the rubber test pieces were still soft and maintained above 70 % of their original tensile strength after hot air aging test at 250 ℃ for 48h.
出处
《合成橡胶工业》
CAS
CSCD
北大核心
1995年第2期100-101,共2页
China Synthetic Rubber Industry
关键词
硅橡胶
聚硅氮烷
硫化胶
填充剂
橡胶
room temperature vulcanized silicone rubber
polysilazane
vulcanizate
filler
mechanical property
heat stability