摘要
本文用络合-沉淀法制备了Y2O3:Eu超微粉末,平均粒径0.04μm~0.1μm,XRD分析为立方晶系。试验结果表明,Y2O3:Eu的平均粒径和相对亮度随焙烧温度的增加而明显增加;超微状态下的Y2O3:Eu相对亮度低;Y2O3:Eu的平均粒径对相对亮度有很大影响。
Y2O3:Eu uitrafine powders were prepared by complex-precipitation method.The mean particle size of Y2O3:Eu is 0.04-0.1um. XRD resuit shows that Y2O3:Eu ultrafine powders are cubic structure. It was found that the mean particle size and relative brightness of Y2O3:Eu increases obviously with the increase of calcination temperature. The relative brightness of Y2O3:Eu ultrafine powders is low. The mean partical size of Y2O3:Eu has great effect on the relative brightness.