摘要
在非晶态Fe76B15Si9合金中加入Ce可明显改变合金的退火脆化倾向,Ce与杂质元素化合生成高熔点的化合物,在晶化过程中成为晶体形成的核心,加快了非均匀成核速率,降低了开始发生晶化的温度,但对其晶化反应进行顺序及晶化产物不产生影响.
Effects of micro-addition of Ce on annealing embrittlement and crystallization of Fe76B15Si9 metallic glasss have been studied. Micro-addtions of Ce obviously affect the susceptibility to embrittlement of Fe76B15Si9 metallic glass and form stable particles in strips by reacting with impurities; these particles act as nucleating center and accelerate the inhomogeneous nucleation, and as a result, lower the crystallization onset temperature for amorphous Fe76B15Si9 alloy; but do not affect the sequence and resultants of crystallization.
出处
《材料研究学报》
EI
CAS
CSCD
1995年第4期313-316,共4页
Chinese Journal of Materials Research
关键词
非晶态合金
稀土
退火脆化
晶化
amorphous alloy rare-earth embrittlement crystallization