摘要
The evolution of microstructure parameters (precipitate size and volume fraction) for two types of Al-Zn-Mg-Cu alloys (7075 and 7055) during aging has been studied by synchrotron-radiation small angle X-ray scattering (SAXS).The results show that the precipitates are only a few nanometers for both alloys ageing even at higher temperature of 160℃ for 72 h (4.44 and 5.82 nm, respectively). The maximum of the precipitate volume fraction increases with in creasing Zn content and is about 0.023～0.028 and 0.052～0.054, respectively. The coarsening of precipitate is consistent with LSW (Lifshitz-Slyozov-Wagner) model even at the initial stage where volume fraction is still varying.The activation energy of coarsening regime has been determined to be about 1.22±0.02 eV and 1.25±0.02 eV for alloys 7075 and 7055, respectively.
The evolution of microstructure parameters （precipitate size and volume fraction） for two types of Al-Zn-Mg-Cu alloys （7075 and 7055） during aging has been studied by synchrotron-radiation small angle X-ray scattering （SAXS）.The results show that the precipitates are only a few nanorneters for both alloys ageing even at higher temperature of 160℃ for 72 h （4.44 and 5.82 nm, respectively）. The maximum of the precipitate volume fraction increases with in creasing Zn content and is about 0.023-0.028 and 0.052-0.054, respectively. The coarsening of precipitate is consistent with LSW （Lifshitz-Slyozov-Wagner） model even at the initial stage where volume fraction is still varying.The activation energy of coarsening regime has been determined to be about 1.22±0.02 eV and 1.25±0.02 eV for alloys 7075 and 7055, respectively.
基金
This research was supported by the National Key Fun-damental Research Project of China(No.G19990649)
National“863”High Technology Program of China(No.2001 A A332030).
关键词
铝合金
显微结构
动态特性
X射线
Small angle X-ray scattering （SAXS）
AI-Zn-Mg-Cu alloys
Ageing
Precipitate size
Volume fraction