摘要
The rolling treatment of steel-mushy QTi3.5-3.5 graphite composite was conducted under different relative reduction at room temperature. The effect of room-temperature rolling on interracial mechanical property of steel-mushy QTi3.5-3.5 graphite composite was studied and the relationship between interracial shear strength and relative reduction was established. The results show that, for steel-mushy QTi3.5-3.5 graphite composite, which consists of 1.2 mm-thick 08AI steel plate and 2.8 mm-thick QTi3.5-3.5 graphite layer, there is a nonlinear relationship between interracial shear strength and relative reduction in graphite layer. When relative reduction is smaller than 1.1%,interracial shear strength increases with increasing the relative reduction. When relative reduction is larger than 1.1%, interracial shear strength decreases with increasing the relative reduction. When relative reduction is 1.1%,the largest interracial shear strength of 145.2 MPa can be obtained.
The rolling treatment of steel-mushy QTi3.5-3.5 graphite composite was conducted under different relative reduction at room temperature. The effect of room-temperature rolling on interracial mechanical property of steel-mushy QTi3.5-3.5 graphite composite was studied and the relationship between interracial shear strength and relative reduction was established. The results show that, for steel-mushy QTi3.5-3.5 graphite composite, which consists of 1.2 mm-thick 08AI steel plate and 2.8 mm-thick QTi3.5-3.5 graphite layer, there is a nonlinear relationship between interracial shear strength and relative reduction in graphite layer. When relative reduction is smaller than 1.1%,interracial shear strength increases with increasing the relative reduction. When relative reduction is larger than 1.1%, interracial shear strength decreases with increasing the relative reduction. When relative reduction is 1.1%,the largest interracial shear strength of 145.2 MPa can be obtained.
基金
supported by the National Natural Science Foundation of China(Nos.50274047 and 50304001)
the Ministry of Education of PRC Foundation
Beijing Jiaotong University Foundation