Hybrid braids of polyglycolide （PGA） and chitosan were prepared by the three-yarn braiding method from PGA and chitosan fiber bundles. These braids were in vitro degraded by incubating them in phosphate buffered saline （ PBS ） at pH 7.4 and 37℃ for 5 weeks. Results suggested that PGA/chitosan hybrid braids degraded significantly. Scanning electron micrographs showed that chitosan fibers in the PGA/chitosan hybrid braid with about 75% PGA in weight （ PGA75/chitosan ）were shaped into gel-like after 5 weeks, but those in the hybrid braid with about 25% PGA in weight（PGA25/chitosan） did not change. After 5 weeks, the ultimate tensile loads of PGA and PGA75/chitosan braids lost almost completely, but those of chitosan and PGA25/chitosan braids remained around 14 N. The PGA/chitosan hybrid braids with higher initial ultimate tensile load would have potential applications in tendon/ligament tissue reconstruction.
Hybrid braids of polyglycolide （PGA） and chitosan were prepared by the three-yarn braiding method from PGA and chitosan fiber bundles. These braids were in vitro degraded by incubating them in phosphate buffered saline （PBS） at pH 7.4 and 37 ℃ for 5 weeks. Results suggested that PGA/chitosan hybrid braids degraded significantly. Scanning electron micrographs showed that chitosan fibers in the PGA/chitosan hybrid braid with about 7500 PGA in weight （PGA75/chitosan） were shaped into gel-like after 5 weeks, but those in the hybrid braid with about 2500 PGA in weight （PGA25/chitosan） did not change. After 5 weeks, the ultimate tensile loads of PGA and PGA75/chitosan braids lost almost completely, but those of chitosan and PGA25/chitosan braids remained around 14 N. The PGA/chitosan hybrid braids with higher initial ultimate tensile load would have potential applications in tendon/ligament tissue reconstruction.
基金
Supported by the Cooperative Project Between Nankai University and Tianjin University, Ministry of Education
Scientific Research Starting Fund for Homecoming Scholars, Ministry of Education.