从生产实际需要出发，与实践相结合，分析连铸板坯中心裂纹和三角区裂纹产生的原因与预防措施，从而减少连铸板坯内裂的发生。
Proceeding from the actual sltuation and combining with the practice of production,the causes of core cracks and triangle zone cracks in slab were analyzed and precautionary mea-sures have been taken to decrease the inner cracks in slabs.