研究了ＤＳＰ材料的制备工艺，成功地制备出抗折强度达１４０ＭＰａ、抗压强度达２４０ＭＰａ、脆性系数达０．５８的新型ＤＳＰ材料；同时，借助于化学分析、压汞测孔仪、扫描电镜和红外光谱等现代测试手段探讨了ＤＳＰ材料的高强机理。
The preparation process of DSP material was studied in detail in the paper, its flexural strength,compressive strength and brittle coefficient were 140MPa, 240MPa and 0. 58 respectively, and the high strength mechanism of DSP moterial was investigated by means of chemical analysis、SEM and IR.