Methyl Methacrylate(MMA) has been filled in the apertures of aligned carbon nanotubes(ACNTs). Then PMMA/ACNTs composites have been synthesized by in-situ polymerization. The SEM results show that carbon nanotubes are well dispersed and directionally arranged in the composites. The electrical conductivities of the parallel direction (parallel with ACNTs) and perpendicular direction (perpendicular with ACNTs) of composites were respectively tested to be 15 S·cm-1 and 4 S·cm-1, so the composites were conductivity anisotropic. Compared with PMMA, the thermal stable temperature of composites in air was improved by 100 ℃,and the thermal con- ductivity of composites was 13.64 times of PMMA.
Methyl Methacrylate(MMA) has been filled in the apertures of aligned carbon nanotubes(ACNTs). Then PMMA/ACNTs composites have been synthesized by in-situ polymerization. The SEM results show that carbon nanotubes are well dispersed and directionally arranged in the composites. The electrical conductivities of the parallel direction (parallel with ACNTs) and perpendicular direction (perpendicular with ACNTs) of composites were respectively tested to be 15 S·cm^-1 and 4 S·cm^-1, so the composites were conductivity anisotropic. Compared with PMMA, the thermal stable temperature of composites in air was improved by 100 ℃,and the thermal conductivity of composites was 13.64 times of PMMA.
出处
《无机化学学报》
SCIE
CAS
CSCD
北大核心
2005年第9期1353-1356,共4页
Chinese Journal of Inorganic Chemistry
基金
国家自然科学基金资助项目(No.10332020)
关键词
定向碳纳米管
PMMA
复合材料
电导率
导热系数
aligned carbon nanotube
PMMA
composite
electrical conductivity
thermal conductivity