A novel compound, （4,4＇-Hbpy）3[NaMo8O26]（4,4＇-bpy）2（H2O）4 1 （bpy=bipydine）, was synthesized by the hydrothermal method. Single-crystal X-ray diffraction shows that compound 1 belongs to the monoclinic system, space group C2/m with a=19.1921（5）, b=18.6931（6）, c=9.3821（3） A° β=104.8020（11）°, V=3254.22（17）A°^3 C50H51Mo8N10NaO30, Mr=2062.52, Z=2, F（000）=2016, μ=1.591 mm^-1 and Dc=2.105 g/cm^3. The final R=0.0283 and wR=0.0912 for 3118 observed reflections （I〉20（I））. Compound 1 contains the β-[Mo8O26]^4-anion, sodium ion, 4,4＇-bpy and lattice crystalline water molecules. The β-[MosO26] units link the sodium ion to form a chain structure. The infinitechains of [Na（Mo8O26）]^3- blocks are surrounded by protonized 4,4＇-bpy cations, 4,4＇-bpy and lattice crystalline water molecules. The 2D-IR correlation spectroscopy study indicates that the stretching vibrations of Mo=O occur more preferentially due to the thermal effect. The TGA analysis shows that compound 1 has high thermal stability.
A novel compound, （4,4＇-Hbpy）3[NaMo8O26]（4,4＇-bpy）2（H2O）4 1 （bpy=bipydine）, was synthesized by the hydrothermal method. Single-crystal X-ray diffraction shows that compound 1 belongs to the monoclinic system, space group C2/m with a=19.1921（5）, b=18.6931（6）, c=9.3821（3） A° β=104.8020（11）°, V=3254.22（17）A°^3 C50H51Mo8N10NaO30, Mr=2062.52, Z=2, F（000）=2016, μ=1.591 mm^-1 and Dc=2.105 g/cm^3. The final R=0.0283 and wR=0.0912 for 3118 observed reflections （I〉20（I））. Compound 1 contains the β-[Mo8O26]^4-anion, sodium ion, 4,4＇-bpy and lattice crystalline water molecules. The β-[MosO26] units link the sodium ion to form a chain structure. The infinitechains of [Na（Mo8O26）]^3- blocks are surrounded by protonized 4,4＇-bpy cations, 4,4＇-bpy and lattice crystalline water molecules. The 2D-IR correlation spectroscopy study indicates that the stretching vibrations of Mo=O occur more preferentially due to the thermal effect. The TGA analysis shows that compound 1 has high thermal stability.
基金
This work was supported by the Foundation of Education Committee of Fujian Province (K02028, JB04049), the State Key Laboratory of Structural Chemistry, and Science and Technology Foundation of Fuzhou University