The chemical compositions of the sludge after treatment are tested by fully chemical analysis techniques. Its crystalline phase structure changes of the sludge calcined at different temperature are characterized by XRD method. Nitrogen gas isothermal adsorption method （77 K） is applied to measure the influences of ammonium bicarbonate on specific surface area and pore structure of activated alumina synthesized from waste aluminum sludge. The result shows that the amount of Al2O3 in the sludge accounts for more than 94%, and Na2Owt% in a 0.1-0.2% range. By calcining raw sludge at 600℃, monophase γ-Al2O3 is obtained. And this can satisfy the performance requirements of activated alumina adsorbent. The specific surface area of the specimen with NH4HCO3 added has expanded from 179 to 249 m^2/g and the pore volume from 0.25 to 1.11 cm^3/g as well as the average pore diameter from 5.6 to 17.8 nm. All these show that NH4HCO3 is an effective pore-expansion agent to remarkably improve the structure and performance of activated alumina synthesized from waste aluminum sludge.
The chemical compositions of the sludge after treatment are tested by fully chemical analysis techniques. Its crystalline phase structure changes of the sludge calcined at different temperature are characterized by XRD method. Nitrogen gas isothermal adsorption method （77 K） is applied to measure the influences of ammonium bicarbonate on specific surface area and pore structure of activated alumina synthesized from waste aluminum sludge. The result shows that the amount of Al2O3 in the sludge accounts for more than 94%, and Na2Owt% in a 0.1-0.2% range. By calcining raw sludge at 600℃, monophase γ-Al2O3 is obtained. And this can satisfy the performance requirements of activated alumina adsorbent. The specific surface area of the specimen with NH4HCO3 added has expanded from 179 to 249 m^2/g and the pore volume from 0.25 to 1.11 cm^3/g as well as the average pore diameter from 5.6 to 17.8 nm. All these show that NH4HCO3 is an effective pore-expansion agent to remarkably improve the structure and performance of activated alumina synthesized from waste aluminum sludge.
基金
department of education of Fujian province