A new niobate Ba6Mg0.67Nb9.33O30 was ssnthesized in the BaO-MgO-Nb2O5 system by solid state reaction at 1350 ℃ for 48 b. The strncture and dielectric properties of Ba6Mg0.67Nb9.33O30 were determined by X-ray pouder diffraction, straining electron microscopy and dielectric measurements. The results show that Ba6Mg0.67Nb9.33O30 belongs to ferroelectric phase of filled tetragonal tungsten bronze structure at room temperature with unit cell parameters ： a = 1. 26052（4） nm , c = 0.40045（2） nm, space group P4bm , calculated density 5 . 707g. cm ^-3 . Ba6Mg0.67Nb9.33O30 belongs to relaxor ,ferroetectrics undergoing diffusive phase transition, and the transition temperature （ Tc ） is 30 ℃ observed at 10 kHz. At room temperature, Ba6Mg0.67Nb9.33O30 eeramic has a high dielectric constant 850 at 1 MHz and a low dielectric loss of 0. 0052.
A new niobate Ba6Mg0.67Nb9.33O30 was ssnthesized in the BaO-MgO-Nb2O5 system by solid state reaction at 1350 ℃ for 48 b. The strncture and dielectric properties of Ba6Mg0.67Nb9.33O30 were determined by X-ray pouder diffraction, straining electron microscopy and dielectric measurements. The results show that Ba6Mg0.67Nb9.33O30 belongs to ferroelectric phase of filled tetragonal tungsten bronze structure at room temperature with unit cell parameters ： a = 1. 26052（4） nm , c = 0.40045（2） nm, space group P4bm , calculated density 5 . 707g. cm ^-3 . Ba6Mg0.67Nb9.33O30 belongs to relaxor ,ferroetectrics undergoing diffusive phase transition, and the transition temperature （ Tc ） is 30 ℃ observed at 10 kHz. At room temperature, Ba6Mg0.67Nb9.33O30 eeramic has a high dielectric constant 850 at 1 MHz and a low dielectric loss of 0. 0052.
基金
FundedbytheNationalNaturalScienceFoundationofChina(N0.50002007),MajorProgramofMOE(No.0201),andFounda-tionofWHUT(2003XJJ204)