After diffusion processing of thermal spraying , aluminum on 20^# steel is discussed in this article. Variations of microstructure, composition as well as mierohardness and corrosion resistatwe of diffusion layer of spray aluminum were explored by means of X-ray diffraction, scanning electron microscopy (SEM) and electron probe microanlysis ( EPMA ) . The result shows that the diffusion layer of spray aluminum consists of η phase ( Fe2Al5 ), ξ phuse ( FeAl2 ), β2 phase ( FeA1 ),β1 plmse ( Fe3Al ) and α pluse from surface to substrate. There are balanced transitions between phases. The layer has extra high hardness and corrosion resistance.
After diffusion processing of thermal spraying , aluminum on 20^# steel is discussed in this article. Variations of microstructure, composition as well as mierohardness and corrosion resistatwe of diffusion layer of spray aluminum were explored by means of X-ray diffraction, scanning electron microscopy (SEM) and electron probe microanlysis ( EPMA ) . The result shows that the diffusion layer of spray aluminum consists of η phase ( Fe2Al5 ), ξ phuse ( FeAl2 ), β2 phase ( FeA1 ),β1 plmse ( Fe3Al ) and α pluse from surface to substrate. There are balanced transitions between phases. The layer has extra high hardness and corrosion resistance.