摘要
用高温显微镜法研究了３Ｃ２Ｓ．３ＣａＳＯ４．ＣａＦ２的熔融特性。结果表明：３Ｃ２Ｓ·３ＣａＳＯ４·ＣａＦ２在１０４０℃左右开始分解出α′Ｃ２Ｓ和ＣａＯ，并于１０９０℃左右大量出现液相，在１２００℃左右时全部熔融，在熔融的同时有少量Ｃ３Ｓ形成。
High temperature microscope analysis was used to study the melting property of 3C 2S·3CaSO 4·CaF 2. The results show that 3C 2S·3CaSO 4·CaF 2 begins to decompose and form α′ C 2S and CaO at about 1040℃. A large amount of liquid phase forms at about 1090℃. At about 1200℃ 3C 2S·3CaSO 4·CaF 2 melts completely, and a little amount of C 3S forms at the same time .
出处
《南京化工大学学报》
1996年第3期17-21,共5页
Journal of Nanjing University of Chemical Technology(Natural Science Edition)
关键词
高温
显微镜
熔融
熟料
水泥
矿化
high temperature microscope\ 3C 2S·3CaSO 4·CaF 2 \ melting\ clinker