SiO2-Al2O3-ZrO2 glasses with different nucleating agents were crystallized under special processing schedule. The microstructure and mechanical properties of the glass-ceramics in SiO2-Al2O3-ZrO2 system were investigated by differential scanning calorimetry, scanning electron microscopy, X-ray diffraction and three-point bending method. The results show that ZrO2 is not an effective nucleating agent in SiO2-Al2O3-ZrO2 system, while TiO2 is effective for the separation of spinel, and P2O5 facilitates solubility of ZrO2 in glass and crystallization. The main crystalline phases of the glass-ceramics are spinel, anorthite and tetragonal zirconia. With the increase of ZrO2 content in the glass, glass-ceramics show higher bending strength （120MPa） than others.
SiO2-Al2O3-ZrO2 glasses with different nucleating agents were crystallized under special processing schedule. The microstructure and mechanical properties of the glass-ceramics in SiO2-Al2O3-ZrO2 system were investigated by differential scanning calorimetry, scanning electron microscopy, X-ray diffraction and three-point bending method. The results show that ZrO2 is not an effective nucleating agent in SiO2-Al2O3-ZrO2 system, while TiO2 is effective for the separation of spinel, and P2O5 facilitates solubility of ZrO2 in glass and crystallization. The main crystalline phases of the glass-ceramics are spinel, anorthite and tetragonal zirconia. With the increase of ZrO2 content in the glass, glass-ceramics show higher bending strength （120 MPa） than others.
基金
Project(2003AA332040)supportedbytheNationalHighTechnologyResearchandDevelopmentProgramofChina
关键词
玻璃
陶瓷
微观结构
机械性能
X光衍射
glass-ceramics
SiO2-Al2O3-ZrO2 system
microstructure
mechanical property