摘要
采用高温固相反应合成了磷酸钡钙∶铈、锰红色荧光粉。借助TG,XRD,荧光粉相对亮度仪、荧光分光光度仪等手段系统研究了合成过程中原料化学组成及配比、合成条件对磷酸钡钙∶铈、锰发光性能的影响。结果表明,荧光粉基质(BaxCa1-x)3(PO4)2具有畸变的Ca3(PO4)2结构。该荧光粉中Ce3+是助激活剂,Mn2+是激活剂,由Ce3+→Mn2+的能量传递使Mn2+激发产生650 nm左右的发射,当Ce3+和Mn2+浓度相等且都为0.15时,荧光粉有最高的红色发射亮度。
Red emitting phosphor （ BaCa）3 （ PO4 ）2 ： Ce, Mn was prepared by solid state reactions. Effect of chemical component, preparation conditions on the performance of the phosphor was studied by using TGDTG, XRD and phosphor relative brightness meter. It is found that the host （BaxCa1-x）3（PO4）2 is present as a distorted Ca3（PO4）2 structure. Ce^3＋ acts as a sensitiser, and Mn^2＋ is activator. By energy transfer from Ce^3＋ to Mn^2＋, Mn^2＋ is activated and emits red light with wavelength around 650 nm. The phosphor powder shows the highest emitting brightness, when the concentrations of Ce^3＋ and Mn^2＋ are both at 0. 15 mol.