摘要
A compared investigation was made on the microstructure and mechanical properties of continuous casting square blanks of BNbRE and U71Mn heavy rail steels having eutectoid composition. The variation of solidified structure of the square blanks was demonstrated by measuring hardness. The observation to the structure and inclusions in the head, waist and base of the hot-rolled rails of the test steels were carried out with optical microscope and SEM. It is found that the casting blanks of both tested steels compose of three areas with constant hardness and three hardness varying areas, and there is considerable P-eutectic structure in the blank of the U71Mn steel. The distribution of the inclusions in the UT1Mn steel rail is mainly oxides in both rail head and rail base, and is mainly MnS in the waist of the rail. There has strong effect of the addition of rare earth elements on them. The discussion on these results was made.
A compared investigation was made on the microstructure and mechanical properties of continuous casting square blanks of BNbRE and U71Mn heavy rail steels having eutectoid composition. The variation of solidified structure of the square blanks was demonstrated by measuring hardness. The observation to the structure and inclusions in the head, waist and base of the hot-rolled rails of the test steels were carried out with optical microscope and SEM. It is found that the casting blanks of both tested steels compose of three areas with constant hardness and three hardness varying areas, and there is considerable P-eutectic structure in the blank of the U71Mn steel. The distribution of the inclusions in the UT1Mn steel rail is mainly oxides in both rail head and rail base, and is mainly MnS in the waist of the rail. There has strong effect of the addition of rare earth elements on them. The discussion on these results was made.