摘要
X70 grade large diameter line pipe with helical and longitudinal seam SAW was developed and used in West-East Pipeline Project of Petrochina. The operation pressure of the pipeline was designed as 10 MPa, with diameter of 1016 mm OD. This project represents the first high-pressure, large diameter and high strength grade gas pipeline in China. All the factors affecting the safety of the pipeline shall be considered. The welds quality of line pipe is very important for safety of the pipeline. Acicular ferrite type X70 grade pipeline steel was adopted for the base material. The welds performances of X70 line pipes with 1016mm OD and 14.6-21.0 mm WT has reached a very high level, especially of low temperature Charpy V impact toughness of welds metal. Welding technique and quality status of X70 line pipe of China are investigated in this paper.
X70 grade large diameter line pipe with helical and longitudinal seam SAW was developed and used in West East Pipeline Project of Petrochina. The operation pressure of the pipeline was designed as 10 MPa, with diameter of 1016 mm OD. This project represents the first high-pressure, large diameter and high strength grade gas pipeline in China. All the factors affecting the safety of the pipeline shall be considered. The welds quality of line pipe is very important for safety of the pipeline. Acicular ferrite type X70 grade pipeline steel was adopted for the base material. The welds performances of X70 line pipes with 1016mm OD and 14.6-21.0 mm WT has reached a very high level, especially of low temperature Charpy V impact toughness of welds metal. Welding technique and quality status of X70 line pipe of China are investigated in this paper.
出处
《广东有色金属学报》
2005年第2期540-544,共5页
Journal of Guangdong Non-Ferrous Metals