摘要
55Q轻轨在使用前由于受到机械加工力而断裂,进行了化学成分、显微组织、夹杂物和低倍检验分析。结果表明,其发生断裂的主要原因是存在较多的小发纹(白点),加之较严重网状组织、夹杂物、晶粒粗大和边部脱碳组织,在机械加工力的共同作用下,导致轻轨发生断裂。
The 55Q light rail was broken because of mechanical process force before use.The chemical composition,microstructure.inclusion and macrographic examination ware analyzed.The results show that the main reason is many little cracks（white spot）exist,and heavy reticulation structure,inclusion,coarse grain and side decarburized stucture.
出处
《物理测试》
CAS
2005年第6期41-43,共3页
Physics Examination and Testing
关键词
55Q轻轨
氢致断裂
网状组织
晶粒粗大
55Q light rail
hydrogen crack
reticulation microstructure
coarse grain