摘要
测定了销－盘式热压Ｓｉ３Ｎ４／３Ｃｒ２Ｗ８Ｖ钢摩擦副在室温干摩擦磨损条件下的的摩擦系数及Ｓｉ３Ｎ４销的磨损系数．对陶瓷销的磨损面进行了ＳＥＭ显微形貌观察、Ｘ射线分析；并探讨了陶瓷销的磨损机理．研究结果表明：Ｓｉ３Ｎ４陶瓷的磨损以微区脆性断裂为主要机理．
The friction coefficient and wear coefficient of hot-pressed Si3N4sliding unlubricated against 3Cr2W8V steel are measured by using a pin-on-discfriction tester at the room temperature. The worn surface of ceramics is bbservedand analyzed by the scanning electron microscope, X-ray diffractometer and electron probe microanalyzer. The wear mechanism of the ceramics is studied. Theresult shows that the wear of St,N. ceramics is mainly attributed to the brittle microfracture mechanism.
出处
《江苏理工大学学报（自然科学版）》
1996年第4期61-64,共4页
Journal of Jiangsu University of Science and Technology(Natural Science)
基金
江苏省自然科学基金
关键词
氮化硅陶瓷
钢
摩擦
磨损
silicon nitride ceramics
steel
friction
wear