摘要
Single phase of Ba1-x MgAl10O17 ： x Eu^2＋ （0.02≤ x ≤ 0. 14） phosphors was first successfully prepared by coprecipitation in aqueous medium with a “reverse strike” method, using oxalic acid and ammonia together as precipitants. Completely crystallized phosphors were obtained at 1300 ℃, which is 300 ℃ lower than the temperature of solid-state reaction. Their photoluminescence was investigated under UV and VUV region, respectively. The emission spectra of Ba1-x MgAl10O17：xEu^2＋ samples excited by 254 or 147 nm showed a characteristic wide band with the peak centred at about 450 454 nm. Optimum emission intensity reached at x = 0.1 and then concentration quenching occurred. The synthesized phosphor shows 10% higher emission intensity than that prepared by solid-state reaction.
Single phase of Ba1-x MgAl10O17 ： x Eu^2＋ （0.02≤ x ≤ 0. 14） phosphors was first successfully prepared by coprecipitation in aqueous medium with a “reverse strike” method, using oxalic acid and ammonia together as precipitants. Completely crystallized phosphors were obtained at 1300 ℃, which is 300 ℃ lower than the temperature of solid-state reaction. Their photoluminescence was investigated under UV and VUV region, respectively. The emission spectra of Ba1-x MgAl10O17：xEu^2＋ samples excited by 254 or 147 nm showed a characteristic wide band with the peak centred at about 450 454 nm. Optimum emission intensity reached at x = 0.1 and then concentration quenching occurred. The synthesized phosphor shows 10% higher emission intensity than that prepared by solid-state reaction.
基金
Project supported bythe National Natural Science Foundation of China (50272026) ,the Excellent Young Teachers ProgramofMOE,China (EYTP) and the Natural Science Foundation of Gansu Province (ZS031-A25-033-C)