The effect of Ce on ignition point of AZ91D magnesium alloy chips was studied. For the AZ91D and the AZ91D-xCe magnesium alloys, changing the sizes of the chips in the range of 58 - 270 μm has a limited influence on ignition point, however, the shift of the content of Ce has much effect on ignition point. Increasing the Ce content, x from 0.15 to 0.25, the ignition point increases with increasing of Ce; however, x from 0.25 to 0.45, the ignition point decreases with increasing of Ce. By the addition of Ce of 0.25 %. the ignition point is raised by 43℃.
The effect of Ce on ignition point of AZ91D magnesium alloy chips was studied. For the AZ91D and the AZ91D-xCe magnesium alloys, changing the sizes of the chips in the range of 58 - 270 μm has a limited influence on ignition point, however, the shift of the content of Ce has much effect on ignition point. Increasing the Ce content, x from 0.15 to 0.25, the ignition point increases with increasing of Ce; however, x from 0.25 to 0.45, the ignition point decreases with increasing of Ce. By the addition of Ce of 0.25 %. the ignition point is raised by 43℃.
基金
Project supported bythe Key Technologies"Fifteen"R&D Programme (2001BA311A05-2)